RoyalTouch300 Nitrile Exam Gloves

Give Your Hands the Royal Treatment

HandPRO® RoyalTouch300™ Powder-Free Nitrile Exam Gloves are uniquely designed to provide the optimal performance and protection you desire. The glove is made from the strongest film possible with ultimate tactile sensitivity, providing the protection you need to work with confidence. The glove is properly contoured and dons easily, delivering unsurpassed strength, chemical resistance and comfort.  Truly the Royal Treatment.

FEATURES AND BENEFITS

  • 300-Count Box – Maximizes space, reduces waste and minimizes cost
  • Revolutionary Design – Provides optimal performance for protection and comfort
  • 100% Nitrile – The strongest film possible with ultimate tactile sensitivity
  • Not Made with Natural Rubber Latex – Will not cause Type I latex allergy
  • Finger-Textured – Tactile sensitivity with a secure grip
  • Royal Blue Color – Easy choice for all members of your team
  • Powder-Free – The standard for health care
  • ASTM F1671 – Passes the viral penetration test
  • FDA 21 CFR Part 177.2600 – Passes FDA and EU food contact tests
  • ITEM NUMBERS/SIZES
  • DOCUMENTATION
  • SPECIFICATIONS
ITEM # SIZE PALM WIDTH +/- 5mm PACKAGING
300 XS 75 300/Box 3000/Case
301 S 85 300/Box 3000/Case
302 M 95 300/Box 3000/Case
303 L 106 300/Box 3000/Case
304 XL 116 250/Box 2500/Case

Specification Sheet/Technical Data Sheet

RoyalTouch300 Spec Sheet

Safety Data Sheet

RoyalTouch300 SDS

Certifications/ComplianceMeets or exceeds ASTM and FDA Standards. Meets MDR (EU) 2017/745. Complies with European Standards EN 455-1:2000, EN 455-2:2015, EN 455-3:2015, and EN 455-4:2009. Complies with PPE Regulation (EU) 2016/425, category III.
MaterialNitrile
ColorBlue
Length9.5" / 240 mm
Cuff Thickness0.04 mm / 1.5 mils
Palm Thickness0.06 - 0.07 mm / 2.3 - 2.7 mils
Fingertip Thickness0.10 - 0.11 mm / 3.9 - 4.3 mils
HandAmbidextrous
LatexNot made with natural rubber latex
Powder FreeYes
TextureFingertip Textured
Tensile Strength27 - 31 MPa (after aging)
Ultimate Elongation480 - 491% (after aging)
Force at Break6.41 - 7.45 Newton (after aging)